| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 无水 | 1.5%水 | |||||
| 基本性能 | 吸水率 | 23℃ | ASTM D-570 | 0.6 | - | % |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.37 | - | --- |
| 泰伯磨耗量 | (1000g,CS-17)23℃ | ASTM D-1044 | 24 | - | mg/1000次 | |
| 机械性能 | 洛氏硬度 | 23℃ | ASTM D-785 | 97 | - | M-标度 |
| 压缩强度 | 80℃ | ASTM D-695 | 1100 | - | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 970 | 830 | Kg/cm2 | |
| 抗剪强度 | 80℃ | ASTM D-732 | 760 | - | Kg/cm2 | |
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 8 | 10 | kg?cm/cm | |
| IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 9 | 14 | kg?cm/cm | |
| IZOD冲击强度 | -40℃ | --- | 60 | 70 | kg?cm/cm2 | |
| IZOD冲击强度 | 23℃，无缺口1/8 | --- | 65 | 78 | kg?cm/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 121 | - | R-标度 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 2350 | 2100 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 1800 | 1350 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 1100 | 900 | Kg/cm2 | |
| 断裂伸长率 | -40℃ | ASTM D-638 | 3.5 | - | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 5 | 5 | % | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 8.5 | - | % | |
| 挠曲强度 | -40℃ | ASTM D-790 | 3000 | - | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 2600 | 1900 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 1750 | 1250 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 85000 | 60000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 50000 | 40000 | Kg/cm2 | |
| 压缩强度 | -40℃ | ASTM D-695 | 2600 | - | Kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 1850 | - | Kg/cm2 | |
| 电气性能 | 体积电阻率 | --- | ASTM D-257 | 1015 | 1012-1013 | Ω.cm |
| 介电强度 | 1/8" | ASTM D-149 | 20 | 17 | KV/mm | |
| 介电常数 | 50Hz | ASTM D-150 | 4.6 | 6.3 | --- | |
| 介电常数 | 103Hz | ASTM D-150 | 4.4 | 5.5 | --- | |
| 介电常数 | 106Hz | ASTM D-150 | 3.9 | 4 | --- | |
| 损耗因数 | 50Hz | ASTM D-150 | 0.02 | 0.08 | --- | |
| 损耗因数 | 103Hz | ASTM D-150 | 0.02 | 0.08 | --- | |
| 损耗因数 | --- | ASTM D-150 | 0.02 | - | --- | |
| 抗电弧性 | 1/8" | ASTM D-495 | 114 | 120 | s | |
| 热 性 能 | UL-94抗燃级 | 1/16" | UL 94 | HB | - | --- |
| 熔点 | --- | 差示扫描测热计DSC | 265 | - | ℃ | |
| 比热 | --- | --- | 0.38 | - | Cal/g?℃ | |
| 导热系数 | --- | --- | 0.02 | - | Kcal/m?hr?℃ | |
| 线性热膨胀系数 | --- | ASTM D-696 | 2_3 | - | ×10-5cm/cm/℃ | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 262 | - | ℃ | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 255 | - | ℃ | |
| 其它性能 | 强化含量 | --- | --- | 30 | - | WT% |